WRC 184 Submerged-Arc-Weld Hardness and Cracking in Wet Sulfide Service
Bulletin / Circular by Welding Research Council, 1973
D. J. Kotecki, D. G. Howden
In stock
More info
Full Description
The codes covering fabrication of virtually all steel structures and pressure vessels require that weldmetal strength equal or exceed base-metal strength. Until recently, however, it was rare that consideration would be given to how much weld-metal strength in excess of base-metal strength was acceptable. There are certain instances, such as when machining of the weld is to be done, or when the weld is to see service in a corrosive environment, that an overly strong or hard weld causes problems. The particular situation of hard welds in corrosive service has caused concern in the petroleum-refining industry and has provided the motivation for the study to be described herein, which was sponsored by the American Petroleum Institute?s Division of Refining, Subcommittee on Corrosion, under the direction of the Task Group on Corrosion Research. A number of failures have occurred recently in plain-carbon-steel (70 ksi ultimate tensile strength or less) vessels containing among other substances, water and hydrogen sulfide, as might occur near the end of a petroleum-refining operation. Frequently, failure has consisted of transverse weld cracking in submerged-arc welds. The cracked welds are usually substantially harder than the base metal. Some instances of weld heat-affected-zone cracking are also known to occur. The cracking mechanism is variously referred to as "sulfide-corrosion cracking," "hydrogen-stress cracking," "stress-corrosion cracking," "wet sulfide cracking," and the like. A combination of high-strength metal, stress and a source of nascent hydrogen (usually a corrosion reaction) seems to be required to produce the cracking.The present study was undertaken to determine:(1) The causes of higher-than-normal hardness in submerged-arc welds in plain carbon steels(2) The levels of strength or hardness which will not be susceptible to sulfide-corrosion cracking
(3) Welding procedures which will assure that nonsusceptible welds be producedConcentration is primarily on weld metal, though some consideration to the weld heat-affected zone is given.